1、耐蚀性研究

1.1  中性盐雾试验   标准: GB/T 10125    SST    Standard: GB/T 10125

锌层厚度为275 g/m2  The coating weight on both sides: 275 g/m2

 

SST

800h

1500h

2000h

GI

 

 

 

ZM

 

 

 

纯锌产品在1100小时出现红锈,镀锌铝镁产品2000小时未出现红锈。

Zinc coating appeared red rust in 1100 hours, Zn-Al- Mg coating had not red rust in 2000 hours。

1.2  盐雾循环加速腐蚀试验   标准: JIS SO M609   CCT    Standard: JIS SO M609

CCT

Cycle

12cyc

24cyc

40 cyc

70 cyc

110 cyc

140 cyc

154 cyc

Z120

 

 

 





ZM100

 

 

 

 

 

 


ZM120

 

 

 

 

 

 

 

Z180

 

 

 





ZM180

 

 

 

 

 

 

 

Z275

 

 

 

 




ZM275

 

 

 

 

 

 

 

 

Z120Z180产品24周期就已经红锈明显,Z275产品在48周期开始出现红锈,ZM10091周期开始出现红锈,从试验结果看,ZM100的耐蚀性优于Z275产品。ZM180ZM275产品140周期才出现轻微锈点。

Z120 and Z180 obviously rusted in 24 cycles。 Z275 appeared red rust in 48 cycles。 ZM100 appeared red rust in 91 cycles。 So ZM100 has better corrosion resistance than Z275。 ZM180 and ZM275 had only a slight red rust point in 140 cycles。

 

1.3  切口部位中性盐雾试验   标准: GB/T 10125     Edge SST    Standard: GB/T 10125

锌层厚度为275 g/m2  The coating weight on both sides: 275 g/m2

 

 

时间

500小时

1000小时

1500小时

2000小时

2500小时

纯锌

Z275

 

 

 

 

 

镀锌铝镁ZM275

 

 

 

 

 

 

镀锌产品在500小时出现红锈,镀锌铝镁产品2000小时无明显红锈。

Zinc coating appeared red rust in 500 hours, Zn-Al- Mg coating had not red rust in 2000 hours.

 

1.4  切口部位盐雾循环加速腐蚀试验  标准: JIS SO M609      Edge CCT    Standard: JIS SO M609

 


厚度

24周期

39周期

54周期

镀锌

Z275

1。0mm

 

 

 

2。0mm

 

 

 

锌铝镁

ZM275

1。0mm

 

 

 

2.0mm

 

 

 

 

2.0mm镀锌产品39周期开始出现红锈,1.0mm产品54周期出现红锈,锌铝镁切口处只有部分白锈,红锈还没有出现。

Red rust began to appear in 2。0mm Zinc coating products after 39 cycles and in1。0mm products after 54 cycles。 Only white rust in edge of Zn-Al- Mg coating after 54 cycles.

 

1.5 拉伸试样盐雾循环加速腐蚀试验  标准: JIS SO M609      drawing sample CCT    Standard: JIS SO M609

 

 


24周期

30周期

39周期

54周期

镀锌

Z180

 

 

 

 

锌铝镁

ZM180

 

 

 

 

 

纯锌产品24周期已经红锈明显,而镀锌铝镁产品54周期才开始出现红锈。

Red rust appeared obviously in Zinc coating sample 24 cycle and Zn-Al- Mg coating began to red rust after 54 cycles.

1.6  耐氨水试验  Ammonia corrosion test

     试验方法:在22℃的5%氨水中浸渍24h后,测定腐蚀减量。试验中试样端面封闭保护。 镀层重量180g/m2。

Test method: Determination of corrosion reduction after impregnation with 24 H in 5 % ammonia at 22 °C. Test specimen end closure protection. The coating weight is 180g/m2。

 

浸泡24小时后,镀锌的减重量为17。022g/m2,镀锌铝镁的减重量为1.017 g/m2,镀锌铝镁的耐氨性能比镀锌更优异。

After 24 hours of immersion, the weight reduction of zinc coating is 17.022g/m2, the weight reduction of Zn-Al- Mg coating is 1。017g/m2, and the ammonia resistance of Zn-Al- Mg coating is better than zinc coating。

 

2、镀锌铝镁产品表面硬度   Hardness

镀锌铝镁硬度明显高于镀锌产品,有效降低加工过程中的划伤和磨损风险。

Zn-Al-Mg coating products have higher surface hardness。 It can reduce scratch and abrasion risk during manufacturing of parts。

 


3、
镀锌铝镁产品表面摩擦系数   Friction 

镀锌铝镁产品初始动摩擦系数和镀锌相差不大,但随摩擦次数的增加变化较小,低的摩擦系数有利于冲压变形。

The initial dynamic friction coefficient of Zn-Al-Mg coating is same as that of zinc coating, but changes little with the increase of friction times。 It is favorable for deformation。

 

4镀锌铝镁产品的焊接性能

产品  Product

焊接电流 CurrentKA

左边界 left border

右边界 right border

焊接电流区间   interval

热浸镀锌钢板 GI  Z100

8.6

10.3

1。7

热浸镀锌铝镁钢板 ZM  Z180

7.5

10.8

3.3

焊点直径:4 (t为钢板厚度),加压力:2。6kN,焊接时间:12循环

 

镀锌铝镁板焊接窗口较镀锌板宽1.6KA

The welding current window of Zn-Al-Mg coating products is 1.6KA wider than that of galvanized sheet.